Store in original sealed containers in a cool dry environment at temperatures between +5°C and +30°C. Do not put excessive loads on top of the products, which would damage the packaging.

Minimum 12 months for part A and 9 months for part B from date of production if stored in original unopened containers. Once opened, product should be used within one week.

Ambient and product temperatures are must be between +15°C and +25°C before mixing. Prior to mixing, stir part A and B separately with a mechanical drill and paddle at a very low speed. Add component B gradually into component A and mix appoximently 3 minutes untill you reach a homogeneous consistency. If necessary, after mixing desired aggregate is added to the mixture and stirred again until a homogeneous mixture is obtained. Pour the contents into a clean container and mix for another couple minutes.

PRIME SURFACES BEFORE APPLICATIONS USING KEMPRİME 2000

WHEN EXPOSED TO DİRECT SUN USE ELASTIPOL 3600 UV TOP COAT FOR UV PROTECTİON.

Avoid application under excessive heat, wind, rain and/or when the ambient and/or substrate temperature is below +10°C or above +30°C. In cold conditions, heaters should be used to increase the ambient temperature an workability of the product. After the mixing procedure, ElastiPol 3500 is poured and spread eventy using serrated trowel. After spreading the material evenly, roll immediately in two directions with a spiked roller to ensure even thickness. Make sure that a continuous coat covers the substrate. If heating is required, use only electric powered warm air blower system. Mixed product should be applied in within 30 minutes. Waiting time between coats should be minimum 10 hours in +20°C and maximum 48 hours. If 48 hours pass and another coat is needed surface should be sanded. The product would be completely cured in minimum 7 days to reach its maximum mechanical and chemical resistance. Reaction times of resin based systems depends on ambient and substrate temperatures as well as relative humidity. Under lower temperatures reaction times are longer which increases pot life, coating intervals and working time. High temperatures contact with water for a minimum of 24 hours. Within this period, contact with water can cause a surface carbonation and/or surface tackiness. In such cases, overall coating should be removed from the floor and renewed.

Surface must be regularly cleaned using rotary brush, mechanical scrubbers, scrubber dryer, high pressure washer, wash and vacuum techniques etc. Using detergents and waxes. Any spillages must be removed immediately.

Clean all tools and application equipment with thinner immediately afet use. Hardened/cures material can only be mechanically removed.